| Alloy | Temper | Thickness / diameter (mm) |
Tensile Strength | Harness Reading HRB |
Webster Hardness Tester (Model B) |
Density kg/mm³ |
Modulus of Elasticity (Mpa) |
|
|---|---|---|---|---|---|---|---|---|
| Ultimate (Mpa) Min | Yield (Mpa) Min | |||||||
| 6063 | T4 | <25 | 130 | 65 | 25 | 0-2 | 2.705 | 69 × 10³ |
| 6063 | T5 | 3| 150 |
110 |
60 |
9-11 |
2.705 |
69 × 10³ |
|
| 6063 | T6 | 3.1| 205 |
170 |
73 |
12-14 |
2.705 |
69 × 10³ |
|
| 6060 | T4 | <25 | 120 | 55 | 23 | 0-2 | 2.705 | 69 × 10³ |
| 6060 | T5 | 3| 150 |
95 |
58 |
10-12 |
2.705 |
69 × 10³ |
|
| 6060 | T6 | 3.1| 190 |
150 |
70 |
11-13 |
2.705 |
69 × 10³ |
|
| 6005 | T4 | <25 | 150 | 80 | 30 | 0-2 | 2.705 | 69 × 10³ |
| 6005 | T5 | 3| 215 |
160 |
65 |
11-13 |
2.705 |
69 × 10³ |
|
| 6005 | T6 | 5| 260 |
200 |
75 |
13-15 |
2.705 |
69 × 10³ |
|
| 6061 | T4 | <25 | 180 | 110 | 40 | 0-2 | 2.705 | 69 × 10³ |
| 6061 | T5 | 3| 240 |
145 |
60 |
11-13 |
2.705 |
69 × 10³ |
|
| 6061 | T6 | 5| 300 |
265 |
90 |
14-16 |
2.705 |
69 × 10³ |
|
| 6061 | T651 | 5| 310 |
275 |
95 |
14-16 |
2.705 |
69 × 10³ |
|
| 6082 | T5 | 5| 260 |
200 |
75 |
12-14 |
2.705 |
69 × 10³ |
|
| 6082 | T6 | 5| 300 |
250 |
90 |
13-15 |
2.705 |
69 × 10³ |
|
| 6082 | T651 | 5| 310 |
260 |
95 |
14-16 |
2.705 |
69 × 10³ |
|
| Alloy | Temper | Thickness / diameter |
Tensile Strength | Elongation (%min 50mm) |
Density kg/mm³ |
Conductivity (IACS) |
|
|---|---|---|---|---|---|---|---|
| Ultimate (Mpa) Min | Yield (Mpa) Min | ||||||
| 1050 | T4 | 2| 75 |
30 |
30% |
2.705 |
57-58% |
|
| 1070 | T4 | 2| 95 |
35 |
35% |
2.705 |
58-60% |
|